Two Major Aspects of Fusion Welding Effects of welding : Effects of welding are those which will always happen when we weld –Residual stressesDistortionFormation of HAZ with metallurgical changes Defects of welding : Defects are those which can be theoretically eliminated, such as –Cracks, Lack…
Category: WELDING
External Defects
Undercut A groove melted into the base metal adjacent to the WELD TOE OR WELD ROOT AND LEFT UNFILLED by weld metal Typical Appearance of Undercut Undercut Adjacent to Fillet Weld Undercut Overlap The projection of weld metal beyond the weld toe or weld root…
Weld defects, their Causes & Remedies
Two Major Aspects of Fusion Welding Effects of welding Defects of welding Effects of welding are those which will always happen when we weld Defects are those which can be theoretically eliminated, such as Residual stresses Cracks, Lack of Fusion, slag inclusions, porosity and undercuts…
TYPES OF WELDING DEFECTS
Incomplete Penetration Incomplete penetration happens when your filler metal and base metal aren’t joined properly, and the result is a gap or a crack of some sort. Check out the Figure below for an example of incomplete penetration. a common case of incomplete penetration Welds…
What is GTAW in welding?
Gas Tungsten Arc Welding GTAW in welding is Gas Tungsten Arc Welding, it is one of the welding types like others SMAW, GMAW and FCAW. GTAW (Gas Tungsten Arc Welding) or TIG (Tungsten Inert Gas) is a welding process which applies a non-consumable tungsten electrode…
UNDERWATER WELDING
UNDERWATER WELDING
Weld Slag Clean Up Requirements for Galvanizing
When welded structures are hot-dip galvanized, the weld area cleanliness significantly affects the quality and appearance of the galvanized coating around the weld. If a coated electrode (i.e. a flux-coated welding wire/rod/stick) is used during welding, all welding flux and slag must be cleaned prior…